TITLE: Study of Rotational Fretting of Quenched and Tempered 4340 Steel
   
COMMITTEE: Dr. Richard Neu, Chair (ME)
Dr. Jeffrey L. Streator (ME)
Dr. Shreyes N. Melkote (ME)
 

SUMMARY

Fretting phenomenon occurs when two bodies in contact undergo small repetitive relative motion such that the localized surface and subsurface material properties are altered leading to damage or failures. Fretting conditions are obtained by controlling externally applied parameters such as load, frequency of displacement, displacement amplitude. Material properties which influence fretting behavior include hardness, ductility, hardening behavior.

Based on fretting conditions and specimen geometry, various fretting modes can be classified. Rotational fretting is one such damage mode, observed in industrial applications such as cable ropes under tension used for support in construction industry and VSVs in compressors.

In the present work, rotational fretting of self-mated AISI 4340 material pair was studied. A novel rotational fretting test set up, capable of operating under various test loads, frequencies, displacement amplitudes and temperatures was used to perform experiments. Specimens were subjected to a combination of normal load and rotational displacement and caused to mutually contact on non-conformal curved surfaces which simulate a bearing or bushing geometry. Fretting results were primarily determined by the frictional torque versus angular displacement plots. The running condition response was linked to the fretting material response regime.

TEM studies revealed varying levels of fretting induced plastic deformation within the fretted contact zone. Good correlation with available literature relating to formation of dislocation cells and presence of high dislocation density in the fretting damaged regions was established. Although quantifying the dislocation density as a damage indicator is a challenge, it is proposed that a microstructural feature based approach has the potential to be developed into a useful tool for life assessment and life prediction studies.